ABSTRACT

A composition of matter comprising an article derived from a composition containing:
         a. from about 30 to 80 wt. % of a polycarbonate component,   b. from about 5 to about 50 wt. % of a polyester component, wherein
 
when polybutylene terephthalate is present in the composition, the polybutylene terephthalate is present in conjunction with at least one other polyester that is not polybutylene terephthalate;
   c. about 2 to about 25 wt. % of an impact modifier; and   d. a gloss reducing effective amount of a multifunctional additive comprising at least one epoxy group.       

     The invention also includes injection molding processes, thermoforming processes for making articles.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a Continuation of U.S. application Ser. No. 11/419,912, filed May 23, 2006, which is a Continuation In Part of and claims priority to U.S. Provisional Application Ser. No. 60/683826 filed on May 23, 2005, and U.S. Original application Ser. No. 11/316227 filed on Dec. 22, 2005, all which are incorporated herein by reference in their entirety.

BACKGROUND OF THE INVENTION

Plastics have been replacing metals and other material products in industry for many years. This is particularly true with respect to automotive parts. The lighter weight of plastics and their flexibility in structural design provide significant motivation to designers and engineers to use plastics. One of the areas in which plastics are contemplated being employed is where paint elimination in a molded part is desirable. However, the look of paint, that is the exterior surface being of low gloss, is also desired. Most plastic materials produce high gloss surfaces when molded. Achieving that low gloss while maintaining the required structural, mechanical, dimensional, chemical resistance, and the like characteristics of the molded part, is difficult to achieve. Of course such desired molded parts are not restricted to automotive use but can be employed in machine housings, appliances, consumer or electronic devices, and outdoor vehicles and devices and any other part needing good mechanical strength and low gloss.

We have succeeded in designing a material that produces a low gloss molded part that satisfies the requirements of its intended use. The look of paint is matched but the advantages of plastic are achieved particularly with respect to performance in higher-heat environments and good mechanical properties. Certain multiple component plastic compositions can be used. Certain additives also enhance the reduction of gloss. Molding conditions can also result in gloss reduction. We have also succeeded in reducing the gloss of an article molded from certain compositions by heating the article under certain conditions. These significant gloss reductions can be achieved even when molding against a polished tool. Substantially uniform low gloss to totally uniform low gloss can be achieved over the molded part surface. The composition can also be readily molded, the viscosity varying according to the requirements of the part to be molded. For example, viscosities below about 500 Pa-s at 271° C. as measured by capillary rheometry following the ISO 11443 standard can be achieved, particularly when large and/or intricate parts are desired.

SUMMARY OF THE INVENTION

The invention relates to a composition of matter comprising an article derived from a composition containing:

-   -   1) from about 30 to 80 wt. % of a polycarbonate component,     -   2) from about 5 to about 50 wt. % of a polyester component,         wherein when polybutylene terephthalate is present in the         composition, the polybutylene terephthalate is present in         conjunction with at least one other polyester that is not         polybutylene terephthalate;     -   3) from about 2 to about 25 wt. % of an impact modifier; and     -   4) from a gloss reducing effective amount of a multifunctional         additive comprising at least one epoxy group.

In one embodiment, the invention relates to a process for making an article by injection molding comprising:

-   -   (a) heating a composition to a temperature that is at least the         melting point of the composition to a viscous liquid     -   (b) injecting the viscous liquid under pressure into a mold         cavity dimensioned to the length, width, and height of a the         article, and     -   (c) allowing the injection molded article to cool and solidify         into the article,     -   (d) removing the article from the mold cavity; wherein         composition comprises:         -   1) from about 30 to 80 wt. % of a polycarbonate component,         -   2) from about 5 to about 50 wt. % of a polyester component,             wherein when polybutylene terephthalate is present in the             composition, the polybutylene terephthalate is present in             conjunction with at least one other polyester that is not             polybutylene terephthalate;         -   3) from about 2 to about 25 wt. % of an impact modifier; and         -   4) a gloss reducing effective amount of a multifunctional             additive comprising at least one epoxy group.

And in another embodiment, the invention relates to a thermo-forming process for making an article comprising:

-   -   (a) extruding a sheet having at least one layer from a         composition comprising:         -   1) from about 30 to 80 wt. % of a polycarbonate component,         -   (2) from about 5 to about 50 wt. % of a polyester component,             wherein when polybutylene terephthalate is present in the             composition, the polybutylene terephthalate is present in             conjunction with at least one other polyester that is not             polybutylene terephthalate;         -   (3) about 2 to about 25 wt. % of an impact modifier; and         -   (4) a gloss reducing effective amount of a multifunctional             additive comprising at least one epoxy group.     -   (b) heating the sheet to a temperature sufficient to soften the         sheet,     -   (c) applying the sheet over a mold dimensioned to the length,         width, and height of the article, and     -   (d) cooling and removing the article from the mold.

Molding conditions can also bring about a reduction in gloss. Good color and low gloss uniformity are hard to obtain at the same time. The compositions accomplish these goals, while maintaining good dimensional stability at high temperature and good mechanical properties. A relatively low viscosity can be achieved which is particularly desirable when molding large or intricate parts, such as those found in automotive applications.

Additionally there is a method for reducing the gloss of an article molded from a composition having at least one aromatic polycarbonate and at least one polyester comprising adding to said composition a gloss reducing effective amount of a multifunctional additive comprising at least one epoxy group, e.g., an epoxy silane or a glycidyl methacrylate modified polyolefin.

Still further, gloss is reduced by lowering the quantity of polybutylene terephthalate (PBT) in a composition.

Additionally, gloss is reduced by increasing the quantity of polyethylene terephthalate (PET) in a composition.

Still further is a composition of a, b, c, and d where at least 5 wt % of the multifunctional additive has reacted with a component of the composition.

Still further, there is a process wherein a, b, c, and d are combined under reactive conditions.

DETAILED DESCRIPTION OF THE INVENTION

The invention is based on the remarkable discovery that it is now possible to produce a molding composition containing polycarbonate and polyester having unexpected low gloss. Articles made from these compositions can also exhibit unexpectedly reduced gloss. Articles made from these compositions can also exhibit highly useful physical and thermal properties. The term article(s) and part(s) are used interchangeably in this application.

The singular forms “a”, “an”, and “the” include plural referents unless the context clearly dictates otherwise.

“Optional” or “optionally” as used herein means that the subsequently described event may or may not occur, and that the description includes instances where the event occurs and the instances where it does not occur.

A “multifunctional additive comprising at least one epoxy group” refers to a compound having at least three reactive sites, e.g., epoxy functional groups, a silane having a reactive site.

The invention relates to a composition of matter comprising an article derived from a composition containing:

-   -   1) from about 30 to 80 wt. % of a polycarbonate component,     -   5) from about 5 to about 50 wt. % of a polyester component,         wherein when polybutylene terephthalate is present in the         composition, the polybutylene terephthalate is present in         conjunction with at least one other polyester that is not         polybutylene terephthalate;     -   6) from about 2 to about 25 wt. % of an impact modifier; and     -   7) from a gloss reducing effective amount of a multifunctional         additive comprising at least one epoxy group.

As further discussed below, the amounts of the components can vary. In one embodiment, the wherein the polycarbonate is from about 45 to 75 wt. %, the polyester is from about 10 to about 45 wt. % and the impact modifier is from about 4 to about 20 wt. %.

Aromatic polycarbonates are employed in the composition of this invention. Typically they are prepared by reacting a dihydric phenol with a carbonate precursor. The dihydric phenols which may be employed to provide such aromatic carbonate polymers are mononuclear or polynuclear aromatic compounds, containing as functional groups two hydroxy radicals, each of which is attached directly to a carbon atom of an aromatic nucleus. Typical dihydric phenols are: 2,2-bis(4-hydroxyphenyl) propane; hydroquinone; resorcinol; 2,2-bis(4-hydroxyphenyl) pentane; 2,4′-(dihydroxydiphenyl) methane; bis(2-hydroxyphenyl) methane; bis(4-hydroxyphenyl) methane; 1,1-bis(4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; fluorenone bisphenol, 1,1-bis(4-hydroxyphenyl) ethane; 3,3-bis(4-hydroxyphenyl) pentane; 2,2-dihydroxydiphenyl; 2,6-dihydroxynaphthalene; bis(4-hydroxydiphenyl)sulfone; bis(3,5-diethyl-4-hydroxyphenyl)sulfone; 2,2-bis(3,5-dimethyl-4-hydroxyphenyl)propane; 2,4′-dihydroxydiphenyl sulfone; 5′-chloro-2,4′-dihydroxydiphenyl sulfone; bis-(4-hydroxyphenyl)diphenyl sulfone; 4,4′-dihydroxydiphenyl ether; 4,4′-dihydroxy-3,3′-dichlorodiphenyl ether; 4,4-dihydroxy-2,5-diphenyl ether; and the like.

Other dihydric phenols used in the preparation of the above polycarbonates are disclosed in U.S. Pat. Nos. 2,999,835; 3,038,365; 3,334,154; and 4,131,575.

Aromatic polycarbonates can be manufactured by known processes; such as, as mentioned above, by reacting a dihydric phenol with a carbonate precursor, such as phosgene, in accordance with methods set forth in the above-cited literature and in U.S. Pat. No. 4,123,436, or by transesterification processes such as are disclosed in U.S. Pat. No. 3,153,008, as well as other processes known to those skilled in the art.

It is also possible to employ two or more different dihydric phenols or a copolymer of a dihydric phenol with a glycol or with a hydroxy- or acid-terminated polyester or with a dibasic acid in the event a carbonate copolymer or interpolymer rather than a homopolymer is desired for use in the preparation of the polycarbonate mixtures of the invention. Branched polycarbonates are also useful, such as are described in U.S. Pat. No. 4,001,184. Also, there can be utilized blends of linear polycarbonate and a branched polycarbonate. Moreover, blends of any of the above materials may be employed in the practice of this invention to provide the aromatic polycarbonate.

One aromatic carbonate is a homopolymer, e.g., a homopolymer derived from 2,2-bis(4-hydroxyphenyl)propane (bisphenol-A) and phosgene, commercially available under the trade designation LEXAN Registered TM from General Electric Company.

Branched polycarbonates are prepared by adding a branching agent during polymerization. These branching agents are well known and may comprise polyfunctional organic compounds containing at least three functional groups which may be hydroxyl, carboxyl, carboxylic anhydride, haloformyl and mixtures thereof. Specific examples include trimellitic acid, trimellitic anhydride, trimellitic trichloride, tris-p-hydroxy phenyl ethane, isatin-bis-phenol, tris-phenol TC (1,3,5-tris((p-hydroxyphenyl)isopropyl)benzene),tris-phenol PA (4-(4-(1,1-bis(p-hydroxyphenyl)-ethyl)alpha, alpha-dimethyl benzyl)phenol), 4-chloroformyl phthalic anhydride, trimesic acid and benzophenone tetracarboxylic acid. The branching agent may be added at a level of about 0.05-2.0 weight percent. Branching agents and procedures for making branched polycarbonates are described in U.S. Pat. Nos. 3,635,895; 4,001,184; and 4,204,047.

Copolyester carbonates are also included within the term polycarbonate. These materials are prepared when a di-functional acid is also included in the preparation, thereby providing ester as well as carbonate bonds in the polymer. For example terephthalic and/or isophthalic acid can be used. When tere- and iso-phthtalic acid are present together with resorcinol as well as the usual bisphenol-A and carbonate precursor, a block polyarylate(ester) within the polycarbonate is formed, see U.S. Pat. No. 6,583,256B2 for example.

A preferred molecular weight (Mw) of the above mentioned polycarbonate is from about 25,000 g/mol to about 75,000 g/mol measured methylene dichloride at 25 OC using a polystyrene standard. For blends where higher flow is desired, a preferred Mw is from about 28,000 g/mol to 60,000 g/mol, more preferred about 35,000 g/mol to 45,000 g/mol. All molecular weights in this application are measured by gel permeation chromatography.

The quantity of aromatic polycarbonate employed in the composition is from about 30 to about 80 wt. % of the composition, preferably about 45 to about 75 wt. %.

Suitable polyesters include those comprising structural units of the following formula:

wherein each R¹ is independently a divalent aliphatic, alicyclic or aromatic hydrocarbon or polyoxyalkylene radical, or mixtures thereof and each A¹ is independently a divalent aliphatic, alicyclic or aromatic radical, or mixtures thereof. Examples of suitable polyesters containing the structure of the above formula are poly(alkylene dicarboxylates), liquid crystalline polyesters, and polyester copolymers. It is also possible to use a branched polyester in which a branching agent, for example, a glycol having three or more hydroxyl groups or a trifunctional or multifunctional carboxylic acid has been incorporated. Furthermore, it is sometimes desirable to have various concentrations of acid and hydroxyl end groups on the polyester, depending on the ultimate end-use of the composition.

The R¹ radical may be, for example, a C₂₋₁₀ alkylene radical, a C₆₋₁₂ alicyclic radical, a C₆₋₂₀ aromatic radical or a polyoxyalkylene radical in which the alkylene groups contain about 2-6 and most often 2 or 4 carbon atoms. The A¹ radical in the above formula is most often p- or m-phenylene, a cycloaliphatic or a mixture thereof. This class of polyester includes the poly(alkylene terephthalates). Such polyesters are known in the art as illustrated by the following patents, which are incorporated herein by reference. U.S. Pat. Nos. 2,465,319; 2,720,502; 2,727,881; 2,822,348; 3,047,539; 3,671,487 3,953,394; and 4,128,526.

Examples of aromatic dicarboxylic acids represented by the dicarboxylated residue A¹ are isophthalic or terephthalic acid, 1,2-di(p-carboxyphenyl)ethane, 4,4′-dicarboxydiphenyl ether, 4,4′ bisbenzoic acid and mixtures thereof. Acids containing fused rings can also be present, such as in 1,4-1,5- or 2,6-naphthalenedicarboxylic acids. The preferred dicarboxylic acids are terephthalic acid, isophthalic acid, naphthalene dicarboxylic acid, cyclohexane dicarboxylic acid or mixtures thereof.

Particularly suitable polyesters are poly(ethylene terephthalate) (“PET”), and poly(1,4-butylene terephthalate), (“PBT”), poly(ethylene naphthanoate) (“PEN”), poly(butylene naphthanoate), (“PBN”), poly(cyclohexanedimethylene terephthalate) (“PCT”), cyclohexanedimethanol modified poly(ethylene terephthalate also known as polycyclohexylenedimethylene ethylene terephthalate) (“PETG” and “PCTG”), and (polypropylene terephthalate) (“PPT”), and mixtures thereof.

When PBT is present in the composition, the polybutylene terephthalate is used in conjunction with at least one other polyester that is not PBT. In this embodiment, suitable weight ratios of PBT to non-PBT polyesters can range from 9:1 to 1:9. In one embodiment, the polyester component does not include PBT. The above-mentioned numerical ranges, as well as the other numerical ranges disclosed in this specification, are understood to be continuous, they include every value between the minimum and maximum values.

Also contemplated herein are the above polyesters with minor amounts, e.g., from about 0.5 to about 25 percent by weight, of units derived from aliphatic acid and/or aliphatic polyols to form copolyesters. The aliphatic polyols include glycols, such as polytetramethylene glycol or poly(ethylene glycol) or poly(butylene glycol). Such polyesters can be made following the teachings of, for example, U.S. Pat. Nos. 2,465,319 and 3,047,539.

The impact modifier employed in the inventive composition is of a core-shell, grafted, or un-grafted nature, or any other type of impact modifier which exists as a separate phase within the blend matrix as observed by a microscopic technique. These impact modifiers reduce the gloss of the resinous composition without any additive present. Such impact modifiers include, but are not limited to, homopolymers as well as polymers from the copolymerization of more than one monomer.

Examples of such impact modifiers are ABS resins, particularly those having a high butadiene content, such as Blendex ABS resins from Crompton, butadiene styrene, nitrile containing rubbers such as Hycar reactive liquid polymers from Noveon Specialty Chemical. Methylmethacrylate butadiene styrene has been used in the system as well. Silicone containing impact modifiers, such as METABLEN S2001, are available from Mitsubishi Rayon Co., Ltd., Tokyo (Japan). A further impact modifier is a LOTADER® resin , for example LOTADER® AX8900 which is sold by Arkema. The resin is a co- or ter-polymer including units of ethylene and glycidyl methacrylate (GMA). An added advantage of LOTADER® resins is colorfastness after exposure to outdoor or accelerated weathering.

Typical ABS impact modifiers are described in US 2004/0059079A1 entitled Enhanced Polymerization Process dated Mar. 25, 2004. Paragraphs 23 to 68 of this publication are incorporated by reference into the specification of the present application. Preferred ABS modifiers are those with high rubber content, such as Blendex 362, which 62% polybutadiene and Blendex 338 which is 70% polybutadiene.

Additional preferred impact modifiers include MBS type modifiers, available from several sources such as Rohm and Haas., LOTADER type modifiers, and a combination of two or more modifiers.

A specific additive(s) can lower the gloss of the molded composition, and any articles made from the composition. The additive is a multifunctional (3 or more reactive groups) agent. At least one of the groups is an epoxy. The second group, if not an epoxy, is a hydroxyl, an isocyantate, a silane, a glycidyl methacrylate modified polyolefin, and the like. Examples of gloss reducing additives are molecules such as a tri-methoxy or tri-ethoxy silane also bearing an epoxy group, for example □-(3,4-epoxycyclohexyl) ethyltriethoxysilane, sold as CoatOSil 1770 by GE. Other examples are □-(3,4-epoxycyclohexyl) ethyltrimethoxysilane, sold as Silquest A-186 by GE and 3-Glycidoxypropyltriethoxysilane, sold as Silquest Y-15589 by GE, Preferred are epoxy groups in a molecule, such as in Coat-O-Sil 1770.

A further example of a preferred gloss reducing additive is a LOTADER® resin. In addition to the impact modification properties previously noted above, the resin is an effective gloss-reducing additive. As noted, multiple epoxy functional groups are present in the polymer.

The quantities of each component are significant and amounts of the materials can affect gloss. Aromatic PC can vary from about 30 to about 80 wt. % of the composition, preferably about 45 to about 75 wt. %. The polyester content is from about 5 to about 50 wt. % of the composition with a more desirable minimum of about 10 wt. %. Generally there is no more than about 45 wt. % for molding applications. If lower viscosity and increased chemical resistance are desired, there should be enough polyester to achieve the desired end properties. The impact modifier is from about 2 to about 25 wt. % of the composition, preferably about 4 to about 20 wt. %. Gloss reduction desired beyond the basic resinous composition is brought about by a minimum amount of gloss reducing additive. The gloss reducing additive(s) (multifunctional additives) can be present in a minimum quantity of about 0.1 wt. % of the composition. When a polymer, such as LOTADER® resin is present in the composition, a desired minimum is about 0.5 wt. %. When a compound, such as an epoxy silane is present in the composition (or an article made from the composition), generally no more than about 5 wt. % is employed. When an epoxy functionalized polymer is present in the composition, such as LOTADER® resin, which has the dual properties of impact modification and gloss reduction, generally no more than about 25 wt. % is employed.

A molding composition of the invention is generally made by combining suitable amounts of the polycarbonate component, the polyester component, the impact modifier, and the multifunctional additive comprising at least one epoxy group in an extruder (or a functionally equivalent compounding device) under suitable conditions. The polycarbonate component, the polyester component, the impact modifier, and the multifunctional additive may be compounded simultaneously, separately, or in combinations containing two or three of the components. The extrusion process can include one or more passes through an extruder

Accordingly, the invention includes embodiments that encompass reaction products that result when the two or three of the components are compounded separately before being combined with the remaining components of the composition. For instance, in one embodiment, the invention includes a composition that includes a reaction product of (i) a multifunctional additive containing at least one epoxy group and (ii) a polyalkylene terephathalate, e.g., polyethylene terephathalate. In another embodiment, the invention includes composition that is a reaction product of (i) a multifunctional additive containing at least one epoxy group and (ii) polybutylene terephathalate. In another embodiment, the invention includes a composition that includes a reaction product of (i) a multifunctional additive containing at least one epoxy group and (ii) a polyester having at least one acid end group. Ordinarily, at least about 5 wt. % of the gloss-reducing additive initially present reacts with a component of the composition, such as a polyester and/or impact modifier.

Molding parts from this composition under ordinary molding conditions, even against a polished tool, will bring about a molded part having a markedly lower gloss than other compositions and, in fact, a low gloss, when desired.

Molded parts (articles) utilizing the composition of this invention include articles such as automotive parts, consumer electronic devices, power tool housings, recreational vehicle parts, power equipment for landscaping and farm use, telecommunication equipment, fitness equipment, and the like. Examples of additional articles that can be molded from a composition of the invention include and are not limited to the following: agricultural equipment and devices, e.g., tractor body panels, airline interior components, arcade housings, jukebox housings & pinball machine housings, archery equipment such as bows and/or arrows, architectural components such as trim and molding, doors (interior and exterior doors), window components, garden equipment such as lawnmower housings and lawnmower plastic components, automotive interior components, baby gear such as strollers, child safety & health equipment, binocular & telescope housings, camcorder housings and camcorder plastic accessories, camera housings and camera plastic components, camping equipment such as tents, cooking utensils, stove plastic parts, hiking equipment, backpacking equipment such as backpack frames, storage containers, canoes, kayaks, rafts, car electronic plastic components such as passenger compartment plastic components and plastic components under the hood and housings, car safety seats, cell phone housings, clock housings, computers & networking equipment such as keyboards, monitor housings, hard disk housings, construction equipment and structural elements, consumer electronics plastic components and devices, corded and cordless power tool housings, cordless power tools, cycling equipment and devices, desktop PC components, digital camera accessories, digital camera housings, digital video recorder housings, display signs such as graphic & logo display signs, display sign housings, DVD Player components & DVD recorder plastic component and housings, electrical & solar equipment and devices, exercise & fitness equipment such as treadmill plastic components, fishing equipment such as fishing poles, food service & retail equipment parts and housings, furniture such as plastic chairs, tables, filing cabinet housings, storage cabinet housings, lamp housings; appliances & fans, gardening tools, golf carts body panels, Global Positioning System (GPS) device housings, gymnastics equipment, health care equipment and health care device housings, heating, cooling & air handling equipment such as ductwork, vents, blowers, home security equipment panels, industrial electrical & test equipment housings, industrial electrical & test equipment panels, keyboards, piano housings, kitchen appliances, lamps, lighting, ceiling fans, laptop housings, notebook housings, lighting & studio equipment, luggage, major appliances, manufacturing & metalworking equipment and devices, monitors & projectors, motor housings, MP3 Player housings & accessories, musical instrument housings and musical instrument plastic components, oral care devices, e.g., toothbrushes, outdoor power equipment, patio & grilling tools, PDAs/Handheld PCs, personal electronic devices, personal security devices, pet houses, pet beds, plumbing & fixtures, pools & spas, pool & spa plastic accessories, printer housings, scanner housings, audio equipment housing and plastic components, projector housings, thermoformed vehicle interiors, radio housings and radio plastic components, television (TV) housings such as flat panel TV housings, telephone housings, recreational vehicle parts, safety glasses, hardhats and other personal safety equipment, satellite radio plastic components and satellite radio plastic housings, satellite dishes, cable TV equipment housings, scooter housings, motorcycles plastic components such as fenders, body panels, shoes and shoe plastic parts, snowmobile plastic components such as snowmobile body panels, speaker housings, plastic toys, train interior components such as train panels, train storage compartments, train benches, train chairs, vacuum cleaner housings and plastic parts, woodworking equipment, other than hand held power tools, such as saw housings, drill press housings.

Such articles can be made by any suitable process. Generally, an article is made by either thermoforming, or injection molding processes.

Injection molding is the most prevalent method of manufacturing for non-reinforced thermoplastic parts, and is becoming more commonly used for short-fiber reinforced thermoplastic composites. Injection molding can be used to produce articles according to the present invention. Injection molding is a process wherein an amount of polymer blend several times that necessary to produce an article is heated in a heating chamber to a viscous liquid and then injected under pressure into a mold cavity. The polymer blend remains in the mold cavity under high pressure until it is cooled and is then removed. The term “injection molding” also encompasses the relatively new advance of reaction injection molding, wherein a two part semi-liquid resin blend is made to flow through a nozzle and into a mold cavity where it polymerizes as a result of a chemical reaction. Injection molding and injection molding apparatii are discussed in further detail in U.S. Pat. Nos. 3,915,608 to Hujick; 3,302,243 to Ludwig; and 3,224,043 to Lameris. Injection molding is the fastest of the thermoplastic processes, and thus is generally used for large volume applications such as automotive and consumer goods. The cycle times range between 20 and 60 seconds. Injection molding also produces highly repeatable near-net shaped parts. The ability to mold around inserts, holes and core material is another advantage. Finally, injection molding generally offer the best surface finish of any process. The skilled artisan will know whether injection molding is the best particular processing method to produce a given article according to the present invention.

As such, the invention contains methods for making articles by injection molding. In one embodiment, the invention encompasses a process for making an article by injection molding comprising: (a) heating a composition to a temperature that is at least the melting point of the composition to a viscous liquid, (b) injecting the viscous liquid under pressure into a mold cavity dimensioned to the length, width, and height of a the article, and (c) allowing the injection molded article to cool and solidify into the article, (d) removing the article from the mold cavity; wherein composition comprises:

-   -   a) from about 30 to 80 wt. % of a polycarbonate component,         -   a. from about 5 to about 50 wt. % of a polyester component,             wherein     -    when polybutylene terephthalate is present in the composition,         the polybutylene terephthalate is present in conjunction with at         least one other polyester that is not polybutylene         terephthalate;         -   b. about 2 to about 25 wt. % of an impact modifier; and         -   c. a gloss reducing effective amount of a multifunctional             additive comprising at least one epoxy group.

Thermo-forming usually begins with plastic sheet or film: sheet thickness tends to be 10 mil (250 μm) and greater; film thicknesses are normally less than 10 mil (250 μm). Extrusion is the most common method of producing sheet and film for thermo-forming; very small amounts are cast or calendered. As used herein, the term “sheet” refers to sheet a layer having a thickness ranging from 0.01 mm, or 0.02 mm to 2.54 cm, or more).

Thermo-forming typically involves heating extruded thermoplastic sheet, film, and profile to its softening heat and forcing the hot and flexible material against the contours of a mold by pneumatic means (differentials in air pressure are created by pulling a vacuum between the plastic and the mold, or the pressure of compressed air is used to force the material against the mold), mechanical means (plug, matched mold, etc.), or combinations of pneumatic and mechanical means.

The process involves (1) heating a sheet (film, etc.) in a separate oven, (2) transferring the hot sheet to a forming press, (3) using automatic machinery to combine heating and forming in a single unit, or (4) a continuous operation feeding off a roll of plastic or directly from the exit of an extruder die (postforming). Almost all the materials are thermoplastic.

These thermoplastics can be reinforced or unreinforced. Almost any thermoplastic can be used, but certain types make it easier to achieve deep draws without tearing or excessive thinning in areas such as corners. Ease of forming depends on material characteristics; it is influenced by minimum and maximum thickness, pinholes, the ability of the material to retain heat gradients across the surface and the thickness, the controllability of applied stress, the rate and depth of draw, the mold geometry, the stabilizing of uniaxial or biaxial deformation, and most important, minimizing the thickness variation of the sheet.

Bending, one of the oldest thermo-forming techniques, is relatively easy to handle. It is often accompanied by joining (adhesive or welding) or mechanical operations (milling, drilling, polishing). If the sheet is heated only locally in the bending operation, no special forming tools are needed. The width of the heating zone and the thickness of the sheet determine the bending radius. Limitations are related to the softening point of the sheet and the intrinsic rigidity of the heated sheet (sag should be minimized). Transparent plastics (such as PMMA and PC) with thicknesses up to 3Y2 in. (90 mm) are frequently bent for use in store displays, staircases, partitions in banks, aircraft windows, and so on. With this type of plastic, if restrictions in the bending area are minimized, the thickness at the bend can remain unchanged.

Thermo-forming processes that can have several advantages over other methods of thermoplastic fabrication. For instance, parts with a large surface area can be formed with relatively low mold and equipment cost, because of the low pressures required. Very thin-walled parts can be readily formed, which is not feasible by any other method. High-volume thin-walled products, such as drinking cups, can be produced at the lowest cost per capital investment, at production rates of 50,000 to over 200,000 units per hour. Low-volume heavy-gauge products, such as computer housings, are competing favorably with injection molding in price, through lower tooling costs, and in product detail with 690 kPa (100 psi) forming pressures. As such, the invention encompasses methods for making articles by thermo-forming processes. In one embodiment, the invention encompasses a thermo-forming process for making an article that involves the steps of:

-   -   (a) extruding a sheet having at least one layer from a         composition comprising:         -   (1) from about 30 to 80 wt. % of a polycarbonate component,         -   (2) from about 5 to about 50 wt. % of a polyester component,             wherein when polybutylene terephthalate is present in the             composition, the polybutylene terephthalate is present in             conjunction with at least one other polyester that is not             polybutylene terephthalate;         -   (3) from about 2 to about 25 wt. % of an impact modifier;             and         -   (4) a gloss reducing effective amount of a multifunctional             additive comprising at least one epoxy group,     -   (b) heating the sheet to a temperature sufficient to soften the         sheet,     -   (c) applying the sheet over a mold dimensioned to the length,         width, and height of the article, and     -   (d) cooling and removing the article from the mold.

The dimensions of low gloss articles can vary. In one embodiment, the size of an article can range from 0.01 square meters to 6 square meters total surface area per side, having a part wall thickness from 0.5 mm to 20 mm, depending on the specific design criteria of each article. These articles may be produced using tools having smooth or rough surfaces in contact with the plastic. When the surface is rough, the roughness may be the result of applying a texture, chemical etching, or mechanical blasting the tool surface. The final roughness of the plastic article may be different than that of the tool. The part roughness may also change as a function of different processing conditions.

The most preferred molded parts utilizing the composition of this invention are injection molded parts having a large surface area and/or parts which in ordinary use are viewed in direct light sources, such as daylight, horizon or cool white fluorescence. These light sources could include a UV component, thereby making color and gloss consistency even more important factors. Examples of these molded parts are vehicle parts such as an instrument panel, a horizontal or vertical vehicle body panel, and the like. Additionally, other smaller vehicular trim parts are preferred, for example bezels, knobs, radio panels, heater control panels, exterior housings, wheel well trim, spoiler, and the like. Other molded parts (articles), where low gloss and good mechanical properties are useful include non-automotive parts, such as consumer or electronic devices, power tools, personal fitness equipment, and transportation vehicles, e.g., motorcycles, carts, trucks. With the composition(s) achieving the low gloss number percentage, the molded part achieves an appearance remarkably similar to a painted low gloss part. Therefore, the part molded from this composition does not need to be painted to achieve such appearance. Such non-painted part provides a substantial cost savings, when compared to a part of comparable design, produced by a similar molding process.

One of the differentiating aspects of these compositions is that gloss, particularly low gloss is uniform or at least substantially uniform throughout the surface of the molded part. Uniformity is typically measured visually by a trained observer. Essentially no brighter or duller regions are seen by the trained observer while viewing the molded part surface. Additionally, variation in gloss can be detected by gloss measuring instruments.

Generally, the more PET the lower the gloss. As impact modifier increases, the gloss is reduced. As PC increases, the gloss increases. As PBT is decreased, generally the gloss is reduced. Interestingly, when PET levels are increased, surface gloss is decreased. When PBT levels are decreased, surface gloss is decreased.

As such, a composition of the invention generally has a gloss reducing effective amount of a multifunctional additive comprising at least one epoxy group (also referred to herein as a “gloss reducing agent.”). The term “gloss reducing effective amount” generally refers to an amount that is sufficient to reduce gloss by at least about 3%, as determined by a gloss meter (e.g., a BYK Gardner micro-TRI-gloss gloss meter) at any angle, e.g., 60°. In another embodiment, the term “gloss reducing effective amount” refers to an amount that is sufficient to reduce gloss by at least about 5%, or a least less than about 10% or at least less than about 15%. In another embodiment, the term “gloss reducing effective amount” refers to an amount of a gloss reducing agent, which decreases gloss by at least about 20%. The artisan will appreciate that the amount of gloss reduction imparted by a composition can be within the above-mentioned ranges, e.g., from at least about 3% to about 5%, or about 10% or about 15% or about 20% or more. The degree to which gloss is reduced can depend on the initial gloss of the plastic article that is being made. Gloss is measured in gloss units.

The absolute gloss value of an article that is achieved by a gloss reduction of at least 3% can vary, depending on the desired application. In one embodiment, as further discussed below, an upper specification limit can be set at 5 gloss units when measured at any angle on a part having a textured surface, such as an interior or exterior automotive part, e.g. an automotive instrument panel. In this instance, any gloss measurement less than 5 gloss units is considered to be low-gloss on a smooth, polished, or textured part when measured at any angle. Other upper specifications can be set, depending on the application.

Gloss is a function of the final roughness of the surface of a molded part. The roughness can be imparted by replicating a rough molding tool surface or be a characteristic of the composition itself, or a combination of the two. Additionally, tool surface roughness and inherent features of the composition can act in combination to produce very low gloss molded articles. Example data provided in this document were measured on parts molded against a polished surface.

The compositions of this invention have distinct advantages over competitive products in the same application area. For example thermoplastic polyolefins have good color and low gloss. However they have poor heat characteristics and mechanical properties. The compositions herein have good color and low gloss but also have good heat and mechanical properties. Examples of heat measurements include HDT and storage modulus. Mechanical properties include tensile modulus, flexural modulus, impact strength, and the like. Rather than painting the surface of the molded part, various pigments can be successfully added to the composition to obtain desired colors. The gloss, particularly low gloss, is uniform or at least substantially uniform over the molded part surface.

Low gloss can be obtained from either a roughened or polished surface of a molding tool. The compositions per se can provide a low gloss surface but gloss can be lowered by other means as well. As previously mentioned, additive(s) can be employed such as an epoxy silane or annealing the molded part will also result in gloss lowering. An example of an additive that will successfully lower gloss is an epoxy silane such as Coat-O-Sil 1770® available from GE. Other multi-functional agents involving an epoxy and/or a silane/siloxane can also be employed. Other means can be employed to lower the gloss than the composition components. Maintaining a relatively moderate heat on the molded part for a period of time, for example a minimum of about 2 minutes, will also bring about a significant gloss reduction. Maintaining a molded part at an elevated temperature such as 85-90° C. for a period of time, post-molding, for example at least about 5 minutes brings about significant gloss reduction.

In one embodiment, the invention relates to a method for reducing gloss that involves heating an article molded from a composition that includes (a) about 30 to 80 wt. % of a polycarbonate component, (b) from about 5 to about 50 wt. % of a polyester component, such that when polybutylene terephthalate is present in the composition, the polybutylene terephthalate is used in conjunction with at least one other polyester that is not polybutylene terephthalate, and (c) about 2 to about 25 wt. % of an impact modifier and a gloss reducing effective amount of a multifunctional additive comprising at least one epoxy group. The additional gloss reduction obtained when the article is heated can be at least about 25% or more. In one embodiment, the gloss reduction can be at least about 25%, or from at least about 25% to about 50%, or more. Unexpectedly, gloss can be reduced when the article is subjected to heating for less than 120 minutes, e.g., less than 30 minutes.

The invention is further described in the following illustrative examples in which all parts and percentages are by weight unless otherwise indicated.

EXAMPLES

Following below are various examples and the procedures used to make these examples.

Standards/Procedures

Tool Surface Finish—Where the term “polished surface” is used in this document, this refers to a tool surface that is finished to an SPI-A1 standard. This finish is typically achieved by the use of a #3 diamond buffing procedure. Preparation of the tool surface in this manner achieves a roughness (Ra) parameter range of 0 to 1 nanometers.

Compounding Procedures—All materials were produced by twin-screw extrusion on a 27 mm or 40 mm diameter line. No unusual compounding processes were employed. All solid raw materials were fed to the extruder in the solid, un-melted form. The raw materials could be fed on individual feeders or as a part of a blend. Blends are then fed on a blend feeder. When liquid additives were a part of the formulation, these were added to the blend and fed on the blend feeder. No pumping of liquids was employed in these experiments. The screw speed and master feed rates employed did not impart excessive specific mechanical energy to the materials during extrusion. Compounding was not considered a vital parameter that could change the outcome in these experiments.

Operational Procedures Used During Molding—Parts were molded on a 85-ton Van Dorn press using small tool inserts, having one or two part cavities. Parts were made using a range of barrel and tool temperature settings. The barrel temperatures were varied from about 274° C. to 302° C. The water set point for the cooler attached to the tool was varied from about 32° C. to about 100° C. Specific details of each experiment are given below.

Oven Treatment Procedures—Some specimens were evaluated after being placed in an oven at 85° C. for a short period of time, such as 5, 10, or 15 minutes. If the initial 200 gloss was greater than about 20 gloss units after molding, this oven treatment lowered the gloss of many specimens by an order of magnitude. This was dependent on molding composition. Typical 20° gloss unit values on polished surfaces dropped from 80 to 8 gloss units or less. This effect was present but less noticeable on textured or stipple surfaces. For this study, no temperatures lower than 85° C. were evaluated. Some molding compositions, such as those containing no PBT, produced gloss values below 5 gloss units at 200, thus requiring no post-molding oven treatment to achieve that level of gloss.

Measurement of Responses—Gloss measurements were taken using a BYK Gardner micro-TRI-gloss portable gloss meter on a 2 inch×3 inch molded chip. The surface of the tool was polished to the SPI A1 standard finish. The gloss meter is designed to make measurements that comply with the ASTM D 523 and ISO 2813. Prior to each measurement, the gloss meter calibration was verified, using the dark calibration standard that is included in the meter storage case. Verification is completed at 20°, 60°, and 85° incident angles. The incident angle of measurement was selected to maximize the sensitivity of the gauge. For polished surfaces, a 20° or 60° angle can be used. If textured or stipple surfaces, a 60° or 85° angle can be chosen. This is consistent with known relationships between surface roughness and angle of measurement.

The general trend of lower gloss with increasing surface roughness predicts that at high levels of roughness, large incident angles are needed to retain sufficient gauge sensitivity. Choosing an angle that is too small will result in a gauge that is not capable of measuring small changes in gloss. In a related way, if the surface roughness is low, smaller incident angles must be used to make the gauge sensitive to small changes in gloss. As gloss approaches 0 gloss units, the gloss meter will become incapable of distinguishing gloss changes at any angle.

Gloss Targets and Specifications—At times an upper specification limit can be set at 5 gloss units when measured at 60° on a part having a textured surface, such as an automotive instrument panel. In this instance, any gloss measurement less than 5 gloss units is considered to be low-gloss If this same part is painted with low gloss paint, the gloss is frequently measured to be in the range of 2 gloss units to 3 gloss units. Therefore, a target gloss value is about 2.5 gloss units at 60° measurement angle on this textured surface. Reducing the gloss on polished or textured surfaces improves the overall perception of gloss and color consistency across molded parts.

Molding Composition/Results Examples 1 to 14 The Effects of Impact Modifier, Polyester, and Epoxy Silane on the Gloss and Viscosity. Examples 1-3

Example Molding Compositions 1 2 3 4 5 6 7 8 9 10 11 12 13 14 PC 62.56 62.56 62.56 63.06 63.06 63.06 62.56 63.06 62.96 61.06 68.56 53.56 63.06 62.56 PET 18.16 18.16 18.16 18.16 18.16 18.16 18.16 18.16 18.16 18.16 18.16 18.16 PBT 18.16 18.16 ABS1 11.00 11.00 11.00 11.00 11.00 11.00 5.00 20.00 MBS 11.00 11.00 METABLEN 11.00 11.00 ABS2 11.00 11.00 CS1770 0.50 0.50 0.50 0.00 0.00 0.00 0.50 0.00 0.10 2.00 0.50 0.50 0.00 0.50 Adds 4.76 4.76 4.76 4.76 4.76 4.76 4.76 4.76 4.76 4.76 4.76 4.76 4.76 4.76 Acid 0.02 0.02 0.02 0.02 0.02 0.02 0.02 0.02 0.02 0.02 0.02 0.02 0.02 0.02 Talc 3.00 3.00 3.00 3.00 3.00 3.00 3.00 3.00 3.00 3.00 3.00 3.00 3.00 3.00 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 Measured Responses Viscosity 465 390 329 390 387 353 381 315 410 707 460 538 397 469 Gloss 20 4.2 14.6 3.7 7.5 32.6 9.6 5.8 14.9 4.6 3.2 10.2 2.3 4.3 2.1 Gloss 60 34.6 60.2 37.5 52.4 79.2 56.8 37.4 63.5 40.6 24.3 59.2 16.9 38.9 16.7

In the examples above (numbers 1 through 14) and those below (numbers 15 through 17), the following descriptions and definitions apply to the raw materials used in each molding composition. PC refers to LEXAN polycarbonate ML8199 from General Electric. PET refers to polyethylene terephthalate 8396 from Invista. PBT refers to polybutylene terephtalate 195 from General Electric. ABS1 is an acrylonitrile butadiene styrene polymer and refers to Blendex 362 from Crompton. METABLEN refers to METABLEN S2001 from Mitsubishi Rayon. ABS2 is an acrylonitrile butadiene styrene polymer and refers to Blendex 338 from Crompton. CS1770 is Beta-(3,4-Epoxycyclohexyl)ethyltriethoxysilane and refers to Coat-O-Sil 1770 from General Electric. “Adds” refers to typical heat stabilizers and pigments used in polymer formulations. Acid refers to a solution of 45% phosphorous acid in water that is added as a catalyst quencher to prevent the trans-esterification of polycarbonate and the polyesters. Other examples of quenchers include phosphoric acid, transition metal phosphates, and other non-acidic species. The effective quantities of quenching agents are well known in the literature. Talc refers to Ultratalc 609 from Specialty Minerals Inc that is added as a nucleant for the polyester resins. The responses measured for each molding composition are as follow. Viscosity refers to the melt viscosity (measured at 271° C. and 640 s⁻¹), following the ISO11443 standard method. Gloss is measured at 20° and 60° using a handheld BYK Gardner micro gloss meter.

The interpretation of these data should be made with both viscosity and gloss goals in mind. Often, the commercially useful molding composition will be one that has both low gloss and low viscosity. Examples 1, 2 and 3 show the effect of various impact modifiers on gloss and viscosity. Examples 4, 5 and 6 show the effect of removing the gloss reducing agent. Examples 7 and 8 show that a PBT containing composition can have its gloss substantially reduced by an additive. Examples 9 and 10 show the effect of increasing the quantity of the gloss reducing agent. Example 10 shows a substantially lower gloss, but at a higher viscosity. The viscosity of example 10 makes this composition unsuitable for injection molding of large part, such as a vehicular instrument panel. However, a smaller or less intricate part molded from the composition of example 10 would have the benefit of very low gloss. Examples 11 and 12 show the effect of increasing impact modifier, particularly on gloss. Examples 13 and 14 show that another ABS impact modifier can be used to achieve low gloss.

Examples 15, 16, and 17

The effect of Coat-O-Sil 1770 epoxy silane and post molding oven treatment of a single molding composition after the compositions were heated for different periods.

Molding compositions 15, 16 and 17 were extruded and molded. These molding compositions differ only in the amount of Coat-O-Sil 1770 present. As the Coat-O-Sil 1770 is increased from 0 to 1.0%, the PC content is lowered to maintain a molding composition total of 100%. PBT, PET and ABS1 are the same as in table 1. PC2 refers to a bisphenol-A polycarbonate having a higher molecular weight than PC1 from table 1. In all other respects, PC2 and PC1 are similar.

After extrusion, color chips were molded and gloss was measured at 20° on the polished side of the chip. These chips were then placed in an oven at 85° C. for varying periods of time. The shortest time period was 15 minutes. The longest time period was 120 minutes.

As the data in Table 2 show, the initial and final gloss values are reduced as Coat-O-Sil 1770 is added to a formulation. The degree of reduction is dependent on the amount of Coat-O-Sil added. In addition, the rate of decrease with oven treatment may change with Coat-O-Sil 1770 level. Also these data show that molding compositions containing both PBT and PET along with a reduced level of ABS can achieve low gloss surfaces when a post molding oven treatment is employed.

TABLE 2 Components/measured gloss values of molding compositions 15, 16, and 17 discussed in the text. Raw Material 15 16 17 PC2 50.00 49.50 49.00 PBT 20.00 20.00 20.00 PET 18.75 18.75 18.75 ABS1 8.75 8.75 8.75 Stabilizers and Pigments 2.50 2.50 2.50 CS1770 0.00 0.50 1.00 Totals 100.00 100.00 100.00 Minutes at 85 C. 20° Gloss 20° Gloss 20° Gloss  0 54.4 35.0 29.2  15 16.5 10.0 6.6  30 14.9 8.8 5.9  60 14.9 9.6 5.5 120 14.2 6.8 5.7

Examples 18 to 20

The gloss effect of different reagents in a single formulation were assessed. These formulations differ only in the kind of gloss additive present.

All additives in table 3 were present in the formulation at the 0.5 wt. % level.

TABLE 3 20° gloss measurements from samples with different gloss additives. PET (IV = PET (IV = Trade Additive .54) .73) name functionality Chemical Name Gloss (20°) Gloss (20°) CoatoSil Multifunctional with Beta-(3,4-Epoxycyclohexyl)ethyltriethoxysilane 3.5 4.3 1770 one epoxy group Silquest Multifunctional with Beta-(3,4-Epoxycyclohexyl)ethyltrimethoxysilane 2.8 3.3 A-186 one epoxy group Silquest Multifunctional with 3-Glycidoxypropyltriethoxysilane 3.4 7.1 Y-15589 one epoxy group ERL 4221 Bifunctional with two 3,4-Epoxycyclohexylmethyl-3,4- 6.8 5.8 epoxy groups epoxycyclohexanecarboxylate AOE X68 Monofunctional with Alpha-olephin epoxide C16-18 11.4 9.2 one epoxy group n-OTEOS Monofunctional n-octadecyltriethoxysilane 12.2 9.2 containing no epoxy groups None No additive None (Control Sample) 6.2 6.8

The data in Table 3 show that multifunctional agents significantly reduce gloss in comparison to bifunctional or mono-functional agents. The data show that the mono-functional agents impart a significantly higher relative to the control sample (no additive). The gloss unit measurements were of parts having smooth (A1) surfaces.

TABLE 4 Examples of Compositions Containing LOTADER AX8900 Resin. Example 18 19 20 High Flow PC 57.74 46.73 46.35 PET Low IV 22.02 18.54 18.42 20% LOTADER/80% PC 15.00 15.00 15.00 VHRG MBS 15.00 15.00 Additives 1.71 1.71 1.71 Talc 3.00 3.00 3.00 CS1770 0.50 0.50 Acid 0.02 0.02 0.02 SUM 100.00 100.00 100.00 Gloss 20 degrees gloss 4.5 6 6.50 60 degrees gloss 35.0 41.2 42.20 Notched IZOD  23° C. Ductility % 0.00 100 100 Impact Strength J/M 146 633 648 −10° C. Ductility % 100 100 Impact Strength J/M 456 420 −20° C. Ductility % 0.00 0 60 Impact Strength J/M 101 307 377 −30° C. Ductility % 0.00 Impact Strength J/M 89.5 Multi-Axial Impact  23° C. Ductility % 60 100 100 Total Energy J 57.1 48.3 48.7 −20° C. Ductility % 0 40 80 Total Energy J 65.4 49.3 54.9

LOTADER as used in the examples of Table 4 is a blend containing 80 wt. % BPA-polycarbonate and 20wt % LOTADER AX8900 resin, which is a terpolymer of ethylene, GMA, and methyl acrylate.

The results of example 18 in Table 4 show that molding compositions containing LOTADER alone do provide lower gloss, but exhibit relatively low impact properties. When MBS is added to a LOTADER containing composition, the results of Example 19 in Table 4 show that LOTADER positively affects gloss reduction in the presence of an MBS impact modifier, when compared to the results of example 5 of Table 1.

The results of example 20 in Table 4 show that the additional of 0.5 wt % Coat-O-Sil 1770 does not bring about further gloss reduction in the tested formulation.

Example 21 Comparative Example

In this Example, the procedure of Example 1 was followed, except that the following composition (in which the only polyester present is polybutylene terephthalate), was evaluated for its gloss characteristics. This composition has been sold by General Electric Company, through its Plastics component, under the VALOX trade name, for several years.

The “Gloss Targets and Specifications” described above were selected for this Example, where a gloss measurement less than 5 gloss units is considered to be low-gloss. The samples that were tested were molded against an A1 (or smooth) surface. Table 5 shows the components of the composition:

TABLE 5 LEXAN Polycarbonate 34.19 Polybutylene terephthalate 37.95 Heat Stabilizer SEENOX 412S 0.40 pentaerythritol betalaurylthiopropionate Processing Aid ETHYLENE 2.00 VINYL ACETATE ELVAX 350 MBS PELLETS, IMPACT MODIFIER 8.00 Heat Stabilizer Irganox 1010 0.06 Halogenated flame retardant additive 14.30 UV-Stabilizer 0.25 Mold Release Additive 0.30 PHOSPHITE STABILIZER 0.20 Processing Aid 0.20 Heat Stabilizer 0.15 LOTADER AX8900 GMA resin 2.00 Total 100.00 Gloss measured on a polished A1 surface 20 degree angle 63 gloss units 60 degree angle 93 gloss units

As can be seen in Table 5, a polyester containing formulation, wherein the only polyester present is polybutylene terephthalate, produces a surface that had a gloss value of 63 gloss units at 20° measurement angle and a gloss value of 93 gloss units at 60° measurement angle, significantly above the less than 5 gloss units low gloss specification.

Example 22

An automotive instrument panel was injection molded from an experimental low gloss formulation as shown below. The instrument panel was molded using a tool that had both textured and non-textured surfaces.

Materials

Two compositions from the materials described below were molded. The first material was a low gloss XENOY formulation of the following composition:

TABLE 6 Material Amount (wt %) 58.37 Polybutylene Terephthalate 21.28 Polyethylene Terephthalate 9.76 ABS Impact modifier, BLENDEX 362, 8.76 available from Crompton Joncryl ADR 4368 epoxy copolymer 0.30 Ultratalc 1.00 SEENOX (412S) 0.05 Phosphorus Acid In Water 0.03 HINDERED PHENOL Antioxidant 0.20 Carbon Black 0.25 100.00

The second material, molded as a control, was LEXAN IP300. LEXAN IP300 is an impact modified polycarbonate material that is currently in use as a material for painted interior automotive parts.

Procedures/Techniques

The instrument panel was made by injection molding, using a 1000-ton Husky molding Press. A composition was heated to a temperature that was at least the melting point of the composition to a viscous liquid. The viscous liquid was then injected under pressure into a mold cavity dimensioned to the length, width, and height of a the article. The injection molded article was allowed to cool and solidify. The article was then removed from the mold cavity.

The formulation of example one was molded at 540F (282° C.) melt temperature and 150F (66° C.) tool temperature.

After molding, parts were removed from the press for measurement of gloss.

The gloss of the part molded from formulation Example 22 was measured to be 42.8 gloss units at a 60-degree measurement angle. The gloss of the part molded from the LEXAN IP300 control material was measured to be 8 gloss units at a 60-degree measurement angle. These measurements were taken at one specific location on a textured surface.

Examples 23-24

In these Examples, low gloss cell phone battery housings were made. A small injection molded part was made, using two colors with a single resin formulation. The part was a cover for a cell phone battery compartment. The tool surface was textured with a fine texture. The tool surface was not chemically etched, prior to use. The two colors used in the example are black and brown

Materials

Two low gloss formulations had the following compositions:

TABLE 7 Example 23 Example 24 Material Black Brown Polycarbonate 66.42 64.09 Polyethylene Terephthalate 18.16 18.16 ABS Impact modifier 11.00 11.00 Seenox 412S 0.10 0.10 Phosphorous Acid Solution 45% 0.02 0.02 Irganox 1010 0.30 0.30 Ultratalc 609 3.00 3.00 CoatOSil 1770 0.50 0.50 Tinuvin 234 0.25 0.25 Carbon Black 0.25 0.20 Pigments Other Than Carbon Black 2.375 100.00 100.00

Procedures/Techniques

Injection molding techniques were used to make these articles. The cell phone battery housing cover was molded on a Husky 1000 ton press, using a melt temperature of 540F (282° C.) and a tool temperature of 150F (66° C.). Each shot of material produced two parts.

Results

After molding, the gloss of the part molded from the formulation from Example 23 was measured to be 2.6 gloss units at a 60-degree measurement angle. The gloss of the article molded from formulation Example 24 was measured to be 3.1 gloss units at a 60-degree measurement angle.

Examples 25-31

These Examples show thermoformed articles being made. Low gloss films were co-extruded as a cap layer over Cycoloy PC/ABS. These sheets were then thermoformed into small parts. The part was a small truck body, similar to a toy.

Materials: The following materials were used:

TABLE 8 Examples 25 26 27 28 29 30 31 Polycarbonate-Resoucinol Copolymer 63.58 58.58 68.58 63.58 58.58 63.58 68.58 Polyethylene Terephthalate 20.00 20.00 20.00 25.00 25.00 15.00 15.00 ABS Impact Modifier 15.00 20.00 10.00 10.00 15.00 20.00 15.00 SEENOX (412S) 0.10 0.10 0.10 0.10 0.10 0.10 0.10 45% Phosphorous Acid Solution in Water 0.02 0.02 0.02 0.02 0.02 0.02 0.02 Irganox 1010 0.30 0.30 0.30 0.30 0.30 0.30 0.30 Epoxy Silane Coatosil 1770 0.50 0.50 0.50 0.50 0.50 0.50 0.50 Tinuvin 234 0.25 0.25 0.25 0.25 0.25 0.25 0.25 Carbon Black 0.25 0.25 0.25 0.25 0.25 0.25 0.25 100.00 100.00 100.00 100.00 100.00 100.00 100.00 60 degree gloss after extrusion 70.7 58.0 86.0 81.0 43.6 56.5 81.0 60 degree gloss after thermoforming 14.7 7.1 9.4 14.2 9.2 17.0 13.5

Procedures/Techniques

These articles were made using a multi-step process. A thin layer of each low gloss formulation was coextruded over a substrate material. After extrusion, the combined multi-layer sheet containing both materials was thermoformed to produce a small part. The part (article) produced in this case was a small truck body, like that often seen in toys.

In this process, the substrate material is typically extruded at a thickness of 0.125 inches (cm). The thinner top layer, typically has a thickness of about 10 mils. This was the case for Examples 25 through 31 The substrate material for Examples 25 through 31 was a PC/ABS resin MC8100, sold by GE Plastics as a commercial product. Both the substrate and the top layer were black.

Results

The gloss measurements results shown in Table 8, are summarized below in Table 9.

TABLE 9 Examples 25 26 27 28 29 30 31 60 degree gloss 70.7 58.0 86.0 81.0 43.6 56.5 81.0 after extrusion 60 degree gloss 14.7 7.1 9.4 14.2 9.2 17.0 13.5 after thermoforming

Results/Discussion

For each multi-layer material, the gloss was measured twice; after extrusion and after thermoforming. All gloss measurements were made on the top surface, where the composition is shown as Examples 25 through 31. All surfaces in Examples 25 through 31 were un-textured, thus producing higher overall gloss values. The results for all formulations indicate that the gloss drops dramatically after thermoforming. All materials in Examples 25 through 31 produced low gloss articles after thermoforming. 

1. A composition of matter comprising, based on the total weight of the composition: a. from about 30 to 80 wt. % of a polycarbonate component, b. from about 5 to about 50 wt. % of a polyester component, wherein when polybutylene terephthalate is present in the composition, the polybutylene terephthalate is present in conjunction with at least one other polyester that is not polybutylene terephthalate; c. about 2 to about 25 wt. % of an impact modifier; and d. from about 0.1 to about 5.0 wt. % of a multifunctional additive comprising an epoxy group and a silane group, or two epoxy groups; wherein the viscosity of the composition is less than about 500 Pa-s at 271° C. as measured by capillary rheometry following the ISO 11443 standard.
 2. The composition of matter in accordance with claim 1, comprising from about 45 to 75 wt. % of the polycarbonate, from about 10 to about 45 wt. % of the polyester, and from about 4 to about 20 wt. % of the impact modifier.
 3. (canceled)
 4. (canceled)
 5. (canceled)
 6. (canceled)
 7. (canceled)
 8. An article comprising the composition of matter of claim 1, wherein the article is an injected molded article.
 9. An article comprising the composition of matter of claim 8, wherein the article is a thermoformed article.
 10. A process for making an article by injection molding comprising: (a) heating a composition to a temperature that is at least the melting point of the composition, to provide a viscous liquid (b) injecting the viscous liquid under pressure into a mold cavity dimensioned to the length, width, and height of a the article, (c) allowing the injection molded article to cool and solidify into the article, and (d) removing the article from the mold cavity; wherein the composition comprises, based on the total weight of the composition: 1) from about 30 to 80 wt. % of a polycarbonate component, 2) from about 5 to about 50 wt. % of a polyester component, wherein when polybutylene terephthalate is present in the composition, the polybutylene terephthalate is present in conjunction with at least one other polyester that is not polybutylene terephthalate; 3) from about 2 to about 25 wt. % of an impact modifier; and 4) from about 0.1 to about 5.0 wt. % of a multifunctional additive comprising an epoxy group and a silane group, or two epoxy groups; and the viscosity of the composition is less than about 500 Pa-s at 271° C. as measured by capillary rheometry following the ISO 11443 standard.
 11. A thermo-forming process for making an article comprising: (a) extruding a sheet having at least one layer from a composition having a viscosity of less than about 500 Pa-s at 271° C. as measured by capillary rheometry following the ISO 11443 standard, and comprising, based on the total weight of the composition: 1) from about 30 to 80 wt. % of a polycarbonate component, (2) from about 5 to about 50 wt. % of a polyester component, wherein when polybutylene terephthalate is present in the composition, the polybutylene terephthalate is present in conjunction with at least one other polyester that is not polybutylene terephthalate; (3) about 2 to about 25 wt. % of an impact modifier; and (4) from about 0.1 to about 5.0 wt. % of a multifunctional additive comprising an epoxy group and a silane group, or two epoxy groups, (b) heating the sheet to a temperature sufficient to soften the sheet, (c) applying the sheet over a mold dimensioned to the length, width, and height of the article, (d) cooling and removing the article from the mold.
 12. The composition of claim 1, wherein the multifunctional additive is beta-(3,4-epoxycyclohexyl)ethyltriethoxysilane.
 12. The method of claim 10, wherein the multifunctional additive is beta-(3,4-epoxycyclohexyl)ethyltriethoxysilane.
 12. The method of claim 11, wherein the multifunctional additive is beta-(3,4-epoxycyclohexyl)ethyltriethoxysilane. 